Suggested number of coating layers
1-2 layers, with a dry paint film thickness of 70-140 μ m. It is better to use high-pressure airless spraying during construction.
Front supporting paint
615-1 and 615-2 aluminum powder chlorinated rubber anti rust paint are used as anti rust primer, 616 chlorinated rubber iron red thick film anti rust paint is used as intermediate layer paint, or H06-4 epoxy zinc rich anti rust paint is used as primer, and 842 epoxy mica iron anti rust paint is used as intermediate layer paint.
Substrate temperature
The substrate temperature must be 3 ℃ above the dew point
Relative humidity not exceeding 85%
Suitable for protecting and decorating the surfaces of various onshore steel structures such as ship waterlines, hulls, superstructures, power plants, steel mills, dock steel structures, chemical plants, bridges, containers, hydraulic steel gates, factory buildings, outer walls of oil storage tanks, dry gas cabinets, etc.
Colour
Orange yellow half light; Green half light; Iron red half light; Green half light; Big red half light; Orange red half light; Steel gray semi gloss; White semi light; Blue gray half light; Light gray half light; Sea blue half light; Medium gray semi light; Black Half Light
Construction parameters
|
Product code
|
Density about
g/cm3
|
Volume Solid
share*%
|
Dry film thickness
μm
|
Wet Film Thickness
μm
|
Theoretical coating amount
m2/kg
|
|
605-3
|
1.53
|
44±3
|
70
|
158
|
4.5
|
|
610-3
|
1.41
|
42±3
|
70
|
168
|
4.2
|
|
626
|
1.36
|
42±3
|
40
|
95
|
8.2
|
|
626-3
|
1.51
|
42±3
|
70
|
167
|
4.3
|
|
629
|
1.14
|
42±3
|
40
|
95
|
8.3
|
|
629-3
|
1.32
|
42±3
|
70
|
167
|
4.3
|
|
634-3
|
1.29
|
42±3
|
70
|
167
|
4.3
|
|
662-3
|
1.51
|
42±3
|
70
|
167
|
4.3
|
|
663
|
1.34
|
40±3
|
40
|
100
|
7.9
|
|
663-3
|
1.41
|
42±3
|
70
|
167
|
4.3
|
|
667-3
|
1.40
|
42±3
|
70
|
167
|
4.3
|
|
670
|
1.24
|
42±3
|
40
|
95
|
8.3
|
|
670-3
|
1.41
|
42±3
|
70
|
167
|
4.3
|
|
671-3
|
1.34
|
42±3
|
70
|
167
|
4.3
|
|
675-3
|
1.42
|
42±3
|
70
|
167
|
4.3
|
|
682-3
|
1.40
|
42±3
|
70
|
167
|
4.3
|